Project Details :
The process comprises of melting of aluminium ingots and scrap in Electric furnace followed by slab casting. Further, the hot rolling process converts preheated slabs into first stage for flat sheets of thickness 80 mm to 50 mm. It is essentially a step towards sheet making. It is followed by cold rolling The cold rolled process rolls and reduces from thickness from 45-50 mm to 30-25 mm, as required to make utensils. The rough edges of cold rolled sheets are cut before going to round cut to make circles. Further, annealing is a very critical stage to release stress developed during rolling stage, the temperature and time of exposure is very critical in this stage. In another operation, the handles are also cast from molten metal and kept in storage.
Note : For Further Information Please Download the Attachment.
|